MAX BOND A/B
THIXOTROPIC
High Strength Epoxy Adhesive
None Sagging Thixotropic
(Will Not Flow At Rest But Easily Spread)
This page contains numerous instructional pictures, videos and links that may take a while to download, please visit our photo sharing site at
WWW.PHOTOBUCKET.COM
USERNAME: ebaypci
PASSWORD: guest
To view the photos and videos directly
Thank you for your patience
You are bidding on a 64 ounce kit
(1 Quart Resin And 1 Quart Curing Agent)
Items receive my be packaged in different container as shown
MAX BOND PRODUCT LINE IS OF EPOXY - POLYAMIDE RESIN SYSTEM DEMONSTRATING EXCELLENT MECHANICAL PROPERTIES SUITABLE FOR MARINE AND AERONAUTICS CONSTRUCTION.
MAX BOND COMES IN 3 VERSIONS
NONE SAG OR THIXOTROPIC GRADE
64 Ounce Kit
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&item=280177201457
2 Gallon kit:
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&rd=1&item=270091522442
MEDIUM VISCOSITY GRADE
32 Ounce kit:
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&rd=1&item=270077788793
2 Gallon kit:
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&rd=1&item=270175927982
MAX BOND LOW VISCOSITY VERSION
32 Ounce Kit:
http://cgi.ebay.com/ebaymotors/ws/eBayISAPI.dll?ViewItem&ih=017&sspagename=STRK%3AMESE%3AIT&viewitem=&item=270118443362
2 Gallon kit:
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&rd=1&item=270085865174
10 Gallon kit:
http://cgi.ebay.com/ws/eBayISAPI.dll?ViewItem&rd=1&item=270087880238
MAX BOND Thixotropic A/B is a general purpose high strength adhesive used in all types of bonding application where excellent water resistance and a wide service temperature exposure is expected. This resin system is an industry "work horse" standard and is the most versatile system available. It can also be used as a reinforcing resin for Fiberglass, AramidsFibers (Kevlar Type) , Carbon Fiber or as crack filling resin. MAX BOND THIXOTROPIC can also be used as surface sealant for many different types of porous substrates and can be applied unto vertical and overhead surface with minimal flow.
MAX BOND THIXOTROPIC does not contain nonreactive plasticizers that typically deteriorates the cured property over time.
Use this resin system as a binder for many other applications ny mixing it with other specialty fillers such as
CONCRETE REPAIR
( MIX 50% SAND AND 50% MAX BOND THIXOTROPIC)
BOAT HULL REPAIR
(MIX 50% MAX BOND THIXOTROPIC, 25% CALCIUM CARBONATE, 25% MICROSPHERES)
INJECTABLE FILLETING ADHESIVE
CRACK FILLING
COMPOSITE BONDING
MAX BOND A/B
THIXOTROPIC
CONCRETE KOI POND REPAIR
MAX BOND THIXOTROPIC was used to repair several concrete Koi pond that leaked at the joints and seams.
Repair Formulation:
|
MATERIALS |
COMPOSITION |
|
MAX BOND THIXOTROPIC PART A |
50 PARTS |
|
MAX BOND THIXOTROPIC PART B |
50 PARTS |
|
CALCIUM CARONATE FILLER |
50 PARTS |
|
ORGANIC PIGMENT |
5 PARTS |
- Premix Part A and Part B until a homogenous blend is achieves
- Add organic pigment until uniform in color
- Add calcium carbonate until uniform
- Apply to precleaned concrete
- Allow to cure for a minimum of 3 days
- Rinse the repair areas with water several times
- Re-fill and condition the water before replacing marine animals
CLICK ON THE PICTURE TO PAUSE OR PLAY PICTURE SLIDE SHOW
MAX BOND A/B THIXOTROPIC
HIGH STRENGTH FABRICATING RESIN
Even with the thixotropic or high viscosity consistency of this resin, it will still wet-out fiberglass and other composite fabrics which makes it and ideal resins system for vertical or multi layer lay-ups.
220 GALLON PLYWOOD AQUARIUM COSTRUCTION USING
MAX BOND THIXTROPIC
MAX ACR A/B (AQUARIUM CONSTRUCTION RESIN)
MAX PCR (WOOD PENETRATING COATING RESIN)
7781 STYLE FIBERGLASS
MAX EPOXY COLORANT
A BRIEF NARRATIVE OF THE CONSTRUCTION PROCESS OF THIS PLYWOOD BASED AQUARIUM CAN BE VIEWED BY
CLICKING ON THE PICTURE TO ACTIVATE PAUSE OR PLAY CONTROLS PICTURE SLIDE SHOW
PROJECT COLLABORATION WITH WITH 'BUCKDOG' AT WWW.MONSETERFISH.COM
-
Non-Critical Mix Ratio
-
Equal Parts by Volume
-
Brush, Roller Coat, Trowel Applied
-
Non-Sag (Thixotropic) For vertical or stay in place bonding
-
Fiberglass Hull Patching
-
Honeycomb core bonding and edge closeout
-
Excellent Impact Resistance
-
Excellent Balance of Strength and Flexibility
-
Water/Salt Water Resistant for Marine/Aero Applications
-
Low Shrinkage, Wide range of service temperature
Usage And Applications Instructions
This item is a thickened version of the MAX BOND Medium Viscosity. It is specially formulated so that the adhesive will not flow allowing the user precise and clean adhesive placement. MAX BOND THIXOTROPIC is paste like in consistency but maintains the adhesion performance of MAX BOND Medium Viscosity.
MAX BOND A/B THIXOTROPIC is vacuum processed to reduce the amount of air entrapment for a stronger structural bond.
Used in hundreds of applications
Marine and Aircraft Bonding
Composite And Metal Bonding
SMC Bonding
Fishing Rod Building
Golf Club Assembly
Concrete Bonding, Patching, Sealing
Electronic Potting, Insulating, Encapsulating
Wood Bonding, Caulking
Composite Adhesive, Laminating
Honeycomb Bonding and Edge Closeout
Just measure out equal amounts of Part A and Part B, mix and apply and allow to cure overnight. It has a 90 minute working time and can be handled in 6 hours. A strong bond will develop in 10 hours of room temperature curing and will fully cure within 24 to 36 hours. Heat curing is also ideal for MAX BOND for a faster cure time and will maintain its non-flowing properties at elevated temperatures. The mixed consistency is similar to peanut butter and is easily applied using a brush, spatula, trowel or injected into place using a syringe.
PHYSICAL PROPERTIES
And
MECHANICAL PROPERTIES
|
Density (Mixed) |
1.10 g/cc |
|
Form and Color Cured |
Translucent Straw Color |
|
Shelf Life |
12 Months |
|
Viscosity Mixed |
15,540 cPs @ 77°F (25ºC) |
|
Mix Ratio |
Equal parts by weight or by volume |
|
Working Time |
120 Minutes @ 77°F
(25ºC 200 gram mass) |
|
Peak Exotherm |
180 °F to 190°F 200 gram mass |
|
Cure Time |
36 Hrs. Minimum
Ultimate properties achieved after
7 Days Cure |
|
Accelerated Cure Schedule |
2 Hrs. @ room temperature plus
120 min. @ 212°F (100oC) |
Samples and specimens were vacuumed cured
24 Hrs. @ room temperature plus
120 min. @ 212°F (100oC)
|
Hardness |
85 to 90 Shore D |
|
Tee-Peel Strength |
6.3 Pounds Per Inch Width |
|
Compressive Strength |
15,800 psi @ 77°F (25ºC) |
|
Tensile Shear Strength |
4,100 psi @ 77°F (25ºC)
2,200 psi @ -112°F (-80ºC)
1450 psi @ 212°F (100ºC) |
|
Elongation |
2.3% Maximum Yield |
|
Tensile Sterngth |
8500 psi (Ultimate @ break) |
|
CHEMICAL RESISTANCE TEST
10 Day Soak Test @ 77°F (25°C)
3% Salt Water
Sulfuric Acid 30%
Nitric Acid
Ammonia 10%
Sodium Hydroxide
Anti-Freeze
Motor Oil Soak
Skydrol |
WEIGHT CHANGE %
1.23
1.9
3.8
3.7
10.00
No Effect
No Effect
No Effect
|
|
Specimen Cure Cycle And Condition |
7 days room temperature
Plus
2 hours 250°F Post Cure |
|
ELECTRICAL PROPERTIES
|
Volume Resistivity |
2.7 x 1012 Ohms-cm (?-cm)
|
|
Dielectric Strength
|
510 Volts/Mil @ 60 Hz. |
|
Dielectric Constant |
3.23 @ 60 Hz | |
SERVICE TEMPERATURE
- 67°F to 230°F
or
- 55°C to 110°C |
VISCOSITY COMPARRISON CHART
|
MATERIAL |
VISCOSITY (centipoises) |
|
Water @ 70° F |
1-5 |
|
Blood or Kerosene |
10 |
|
Anti-Freeze or Ethylene Glycol |
15 |
|
Motor Oil SAE 10 or Corn Syrup |
50-100 |
|
Motor Oil SAE 30 or Maple Syrup |
150-200 |
|
Motor Oil SAE 40 or Castor Oil |
250-500 |
|
Motor Oil SAE 60 or Glycerin |
1,000-2,000 |
|
Corn Syrup or Honey |
2,000-3,000 |
|
Blackstrap Molasses |
5,000-10,000 |
|
Hershey Chocolate Syrup |
10,000-25,000 |
|
Heinz Ketchup or French’s Mustard |
50,000-70,000 |
|
Tomato Paste or Peanut Butter |
Track up to 10 items on this computer in 
)